Structuring of polyurethane materials using different network precursors

dc.contributor.advisorBudinski-Simendić, Jaroslava
dc.contributor.otherRadičević, Radmila
dc.contributor.otherBudinski-Simendić, Jaroslava
dc.contributor.otherStoiljković, Dragoslav
dc.contributor.otherMesaroš-Sečenji, Katalin
dc.contributor.otherMarinović-Cincović, Milena
dc.creatorPavličević, Jelena
dc.date.accessioned2018-10-03T14:23:37Z
dc.date.available2018-10-03T14:23:37Z
dc.date.available2020-07-03T13:52:43Z
dc.date.issued2010-06-25
dc.identifier.urihttps://nardus.mpn.gov.rs/handle/123456789/9956
dc.identifier.urihttps://www.cris.uns.ac.rs/DownloadFileServlet/Disertacijadisertacija.pdf?controlNumber=(BISIS)81933&fileName=disertacija.pdf&id=436&source=NaRDuS&language=srsr
dc.identifier.urihttps://www.cris.uns.ac.rs/record.jsf?recordId=81933&source=NaRDuS&language=srsr
dc.identifier.urihttps://www.cris.uns.ac.rs/DownloadFileServlet/IzvestajKomisije152447309468445.pdf?controlNumber=(BISIS)81933&fileName=152447309468445.pdf&id=11219&source=NaRDuS&language=srsr
dc.description.abstractU ovom radu, sintetisani su poli(uretan-izocijanuratni) elastomeri sa kovalentnim čvorovima, katalitičkom ciklotrimerizacijom teleheličnih diizocijanata kao prekursora mreže na osnovu 2,4-toluen-diizocijanata, α,ω-dihidroksipoli(oksipropilen)diola i monoola dietilenglikolmonometiletra. Dobijeni su i termoplastični segmentirani poliuretani, sa čvorovima fizičkog umreženja, jednostepenim postupkom i metodom prepolimerizacije, reakcijom dve vrste alifatskog polikarbonatnog diola, koji se razlikuju u strukturi lanca, heksametilen-diizocijanata i produživača lanca (1,4-butandiola). Sintetisana je i serija poliuretanskih hibridnih materijala, dodatkom 1% m/m nanočestica organski modifikovanih glina (montmorilonita i bentonita). Prioritet rada je bio da se utvrdi uticaj udela elastično aktivnih i visećih lanaca na dinamičko-mehanička svojstva, toplotnu stabilnost i svojstva prigušenja poliuretanskih mreža sa izocijanurat (heksahidro-1,3,5-triazin-2,4,6-trion) prstenovima, kao čvorovima. Takođe, cilj istraživanja je bio da se ispita uticaj odnosa reaktivnih grupa diizocijanata, polikarbonatne komponente i produživača lanca, kao i dodatka nanočestica na svojstva površine, morfologiju, dinamičko-mehanička i toplotna svojstva segmentiranih neojačanih i ojačanih elastomera. Toplotna degradacija poli(uretanizocijanuratnih) mreža i segmentiranih termoplastičnih poliuretana praćena je neizotermskim ispitivanjima, koristeći istovremenu termogravimetrijsku i masenu analizu (TG-MS), kao i istovremenu termogravimetriju i diferencijalno skenirajuću kalorimetriju (TG-DSC). Viskoelastična svojstva i svojstva prigušenja dobijenih poliuretanskih elastomera su ispitivana pomoću dinamičko-mehaničke analize (DMA). Toplotno ponašanje segmentiranih poliuretana i nanokompozita, dobijenih jednostepenim postupkom sinteze, je proučavano modulovanom diferencijalno skenirajućom kalorimetrijom (MDSC). Temperatura prelaska u staklasto stanje i termoplastična svojstva neojačanih i ojačanih poliuretanskih materijala, dobijenih postupkom prepolimerizacije, određeni su primenom diferencijalno skenirajuće kalorimetrije (DSC). Hemijska struktura i formiranje vodoničnih veza dobijenih elastomera proučavane su koristeći Furijeovu transmisionu infracrvenu spektroskopiju (FTIR). Uticaj udela tvrdih segmenata na morfologiju i svojstva površine segmentiranih poliuretana, ispitivan je pomoću mikroskopije atomskih sila (AFM). Stepen kristalnosti uzoraka i dispergovanje nanočestica u dobijenim hibridnim materijalima su odreñeni primenom metode rasipanja X-zraka pod širokim uglom (WAXS).sr
dc.description.abstractIn this work, poly(urethane-isocyanurate) elastomers, with covalent junction points, were synthesized by catalytic cyclotrimerization of telechelic diisocyanates as network presursors based on 2.4-tolylenediisocyanate, a,w,dihydroxypoly(oxypropylene) and monool component 2-(2-metoxyetoxy)ethanol. Thermoplastic polyurethanes, with physical crosslinking, were obtained by one-step technique and pre-polimerization method, using two aliphatic polycarbonate diols (differening in chain constitution), hexamethylene-diisocyanate and chain extender (1,4-butane diol) as reactive components. One serie of polyurethane hybrid materials was prepared by addition of 1 wt. % of organically modified clay nanoparticles (bentonite and montmorillonite). The goal of this work was to investigate the influence of elastically active and dangling chains content on thermal stability, dynamic mechanical and damping properties of polyurethane networks with heat-resistant isocyanurate-(hexahydro-1,3,5-triazin-2,4,6-trion) rings, as crosslinks. The aim was also to determine the influence of diisocyanate, macrodiol and chain extender reactive groups’ ratio and nanoparticles addition on surface properties, morphology, dynamic mechanical and thermal properties of obtained segmented unfilled and filled elastomers. Thermal degradation of poly(urethane-isocyanurate) networks and segmented thermoplastic polycarbonate-based polyurethanes was investigated by nonisothermal analysis, using thermogravimetry coupled with mass spectroscopy analysis (TG-MS) and thermogravimetry coupled with differential scanning calorimetry (TG-DSC). Viscoelastic and damping properties of obtained polyurethane elastomers were estimated by dynamic mechanical measurements (DMA). Modulated differential calorimetry (MDSC) was used to investigate thermal behavior of segmented polyurethanes and nanocomposites, synthesized using one-step technique. The glass transition temperature and thermoplastic properties of unfilled and filled polyurethane materials, prepared by pre-polimerization procedure were assessed by differential scanning calorimetry (DSC). Fourier transform infrared spectroscopy (FTIR) was used to investigate the hydrogen bond formation and chemical structure of prepared segmented elastomers. The investigation of the influence of hard segment content on morphology and surface topography of prepared segmented elastomers sheets was done by atomic force microscope (AFM). In order to determine the degree of cristallinity and to evaluate the dispersion of montmorillonite and bentonite in the polyurethane matrices, the prepared hybrid materials were characterized by wide angle X-ray scattering (WAXS).en
dc.formatapplication/pdf
dc.languagesr (latin script)
dc.publisherУниверзитет у Новом Саду, Технолошки факултетsr
dc.rightsopenAccessen
dc.rights.urihttps://creativecommons.org/licenses/by/4.0/
dc.sourceУниверзитет у Новом Садуsr
dc.subjectPrekursori mrežasr
dc.subjectNetwork precursorsen
dc.subjectpoly(urethaneisocyanurate)en
dc.subjectorganically modified clay nanoparticlesen
dc.subjectsegmented polyurethanesen
dc.subjecthybrid materialsen
dc.subjectpoli (uretanizocijanurati)sr
dc.subjectnanočestice organski modifikovanih glinasr
dc.subjectsegmentirani poliuretanisr
dc.subjecthibridni materijalisr
dc.titleStrukturiranje poliuretanskih materijala primenom različitih prekursora mrežasr
dc.title.alternativeStructuring of polyurethane materials using different network precursorsen
dc.typedoctoralThesisen
dc.rights.licenseBY
dcterms.abstractБудински-Симендић, Јарослава; Будински-Симендић, Јарослава; Радичевић, Радмила; Стоиљковић, Драгослав; Месарош-Сечењи, Каталин; Мариновић-Цинцовић, Милена; Павличевић, Јелена; Структурирање полиуретанских материјала применом различитих прекурсора мрежа; Структурирање полиуретанских материјала применом различитих прекурсора мрежа;
dc.identifier.fulltexthttp://nardus.mpn.gov.rs/bitstream/id/39820/Disertacija17629.pdf
dc.identifier.fulltexthttp://nardus.mpn.gov.rs/bitstream/id/39821/IzvestajKomisije17629.pdf
dc.identifier.fulltexthttps://nardus.mpn.gov.rs/bitstream/id/39821/IzvestajKomisije17629.pdf
dc.identifier.fulltexthttps://nardus.mpn.gov.rs/bitstream/id/39820/Disertacija17629.pdf
dc.identifier.rcubhttps://hdl.handle.net/21.15107/rcub_nardus_9956


Документи за докторску дисертацију

Thumbnail
Thumbnail

Ова дисертација се појављује у следећим колекцијама

Приказ основних података о дисертацији