Fatigue crack growth in T welded joint of aluminium alloy
Rast zamorne prsline u T zavarenom spoju legure aluminijuma.
Doktorand
Kraedegh, Abubakr M. AbdulgadrMentor
Sedmak, AleksandarČlanovi komisije
Radaković, ZoranGrbović, Aleksandar
Veg, Emil
Burzić, Zijah
Metapodaci
Prikaz svih podataka o disertacijiSažetak
U ovom radu su prikazani inicijacija i rast prsline u T spoju ploče od aluminijumske legure
AA2024 –T351, zavarenom mešanjem trenjem (Friction Stir Welding - FSW), primenom
mehanike loma. Svi analizirani modeli su napravljeni od legure 2024-A351. Osobine materijala
i dimenzije u oblasti FSW spoja su usvojene na osnovu dostupnih eksperimenata...
In this present work, application of fracture mechanics is used to present a fatigue crack
initiation and growth of friction stir welded (FSW) T joint plate made of aluminum alloy
AA2024 –T351. All analyzed models are made from aluminum alloy 2024-T351.The
properties of materials in the areas of joints and geometry measures of FSW joint are adopted
from available experiments...