The correlation of rheocasting process parameters - structure and properties of hypereutectic aluminium-silicon alloys.

dc.contributor.advisorAćimović-Pavlović, Zagorka S.
dc.contributor.otherRaić, Karlo
dc.contributor.otherDojčinović, Marina
dc.contributor.otherTerzić, Anja
dc.creatorĆosić, Milena M.
dc.date.accessioned2016-08-27T16:05:36Z
dc.date.available2016-08-27T16:05:36Z
dc.date.available2020-07-03T09:24:08Z
dc.date.issued2014-04-10
dc.identifier.urihttp://eteze.bg.ac.rs/application/showtheses?thesesId=3691
dc.identifier.urihttps://nardus.mpn.gov.rs/handle/123456789/6365
dc.identifier.urihttps://fedorabg.bg.ac.rs/fedora/get/o:12505/bdef:Content/download
dc.identifier.urihttp://vbs.rs/scripts/cobiss?command=DISPLAY&base=70036&RID=45871375
dc.description.abstractNadeutektičke Al-Si legure su našle široku primenu u automobilskoj i avio industriji zbog odlične otpornosti na koroziju i habanje, niskog koeficijenta termičkog širenja, dobre čvrstoće, odličine livkosti i male gustine. Svojstva nadeutektičkih Al – Si legura zavise od karakteristika njihove livene mikrostrukture koja se mogu poboljšati mikrostrukturnim promenama. U okviru ovog rada poboljšanje mehaničkih svojstava (tvrdoće) i kavitacione otpornosti realizovani su sledećim promenama: promenom veličine, morfologije (oblika) i raspodele primarnih i eutektičkih Si čestica. Da bi se postigla transformacija dendritne u ne-dendritnu strukturu, poluočvrsli rastop AlSi18CuMgNi legure izlagan je dejstvu smicajnih sila nastalih mehaničkim mešanjem. Mešanje rastopa legure, primenom mešača oblika ploče, izvedeno je u temperaturnom intervalu između solidus i likvidus temperature sa postepenim povećanjem brzine mešanja od 500 do 1500 o/min. Odlivci kompozita AlSi18CuMgNi/SiC dobijeni su primenom kompokasting postupka. Kao ojačivač korišćen je SiC sa prosečnom veličinom čestica 30 μm. Kavitaciona otpornost materijala, kao što su legure metala, zavise od mehaničkih svojstava posebno tvrdoće. Reokast uzorci dobijeni pri većoj brzini hlađenja i smicanja pokazali su najveću tvrdoću. Vrednost tvrdoće reokast uzoraka je opadala sa porastom vremena mešanja usled aglomeracionih procesa. Kavitaciona otpornost konvencionalnih (gravitaciono kokilno livenje), reokast i odlivaka kompozita procenjena je primenom ultrazvučne vibracione metode sa stacionarnim uzorkom. Gubitak mase odlivaka za vreme ispitivanja određivan je analitičkom metodom. Mikrostruktura i morfologija oštećene površine testiranih materijala ispitivane su primenom optičkog (OM) i skenirajućeg elektronskog mikroskopa (SEM)...sr
dc.description.abstractHypereutectic Al-Si alloys are widely used in the automobile and aerospace industries because they exhibit excellent wear and corrosion resistance, low coefficient of thermal expansion, good strength, excellent castability and low density. The properties of hypereutectic Al-Si alloys depend on the characteristics of their cast microstructure and they can be improved by microstructure changes. In this paper, the improvements in the mechanical properties (hardness), cavitation resistance were realized with the following changes: size, morphology (or shape), and distribution of primary and Si eutectic particles. The semi-solid melt of the AlSi18CuMgNi alloy was exposed to shear forces (caused by mechanical mixing) in order to achieve transformation of dendritic into the non-dendritic structure. Mixing of the melt (active part of the paddle stirrer) was performed in the temperature range between liquidus and solidus temperatures with a gradual increase in mixing speed from 500 to 1500 rpm. Aluminium matrix composite AlSi18CuMgNi/SiC castings were prepared using the compocasting technique. The reinforcements used were silicon carbide (SiC) particles with an average size of 30 μm. The cavitation resistance of materials such as metal alloys depends of mechanical properties (especially hardness) and microstructure. The maximum in hardness for rheocast sample obtained by higher cooling rate and higher stirring speed was achieved. The hardness values for rheocast sample decrease with increasing the stirring time due to agglomeration process. The cavitation resistance of conventional, rheocast and composite castings was evaluated by using an ultrasonically induced cavitation test method. Mass loss of castings during testing time was measured by an analytical method. Microstructures and morphology of damaged surfaces of tested materials were examined using of optical microscopy (OM) and scanning electron microscopy (SEM)...en
dc.formatapplication/pdf
dc.languagesr
dc.publisherУниверзитет у Београду, Технолошко-металуршки факултетsr
dc.rightsopenAccessen
dc.rights.urihttps://creativecommons.org/licenses/by-nc-nd/4.0/
dc.sourceУниверзитет у Београдуsr
dc.subjectAl –Si leguresr
dc.subjectAl-Si alloysen
dc.subjectreokastingsr
dc.subjectkompokastingsr
dc.subjectmikrostrukturasr
dc.subjectkavitaciona otpornostsr
dc.subjectrheocastingen
dc.subjectcompocastingen
dc.subjectmicrostructureen
dc.subjectcavitation resistanceen
dc.titleKorelacija parametara Rheocasting procesa-strukture i svojstva nadeutektičkih aluminijum-silicijum legurasr
dc.titleThe correlation of rheocasting process parameters - structure and properties of hypereutectic aluminium-silicon alloys.en
dc.typedoctoralThesisen
dc.rights.licenseBY-NC-ND
dcterms.abstractAћимовић-Павловић, Загорка С.; Терзић, Aња; Раић, Карло; Дојчиновић, Марина; Ћосић, Милена М.; Корелација параметара Рхеоцастинг процеса-структуре и својства надеутектичких алуминијум-силицијум легура; Корелација параметара Рхеоцастинг процеса-структуре и својства надеутектичких алуминијум-силицијум легура;
dc.identifier.fulltexthttps://nardus.mpn.gov.rs/bitstream/id/18432/Disertacija4335.pdf
dc.identifier.fulltexthttp://nardus.mpn.gov.rs/bitstream/id/18432/Disertacija4335.pdf
dc.identifier.rcubhttps://hdl.handle.net/21.15107/rcub_nardus_6365


Документи за докторску дисертацију

Thumbnail

Ова дисертација се појављује у следећим колекцијама

Приказ основних података о дисертацији